①原料描述部分
| 规格级别 | 高流动, 通用 | 外观颜色 | |
| 该料用途 | |||
| 备注说明 | 特性：高流动性 | ||
| 加工条件 |
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 成型收缩率 | ASTM D-955 | 0.2-0.6 | ||
| 熔体流动速率 | 220℃ 10kg | ASTM D-1238 | 25 | g/10min | |
| 比重 | ASTM D-792 | 1.07 | |||
| 熔体流动速率 | 220℃ 5kg | ASTM D-1238 | 2.5 | g/10min | |
| 机械性能 | IZOD冲击强度 | 1/8" Notched | ASTM D-256 | 2.0 | kg.cm/cm |
| 洛氏硬度 | ASTM D-785 | 122 | R | ||
| 拉伸强度 | ASTM D-638 | 720 | kg/cm2 | ||
| 弯曲强度 | ASTM D-790 | 1350 | kg/cm2 | ||
| 伸长率 | ASTM D-638 | 8 | % | ||
| 弯曲模量 | ASTM D-790 | 40000 | kg/cm2 | ||
| IZOD冲击强度 | 1/4〃 Notched | ASTM D-256 | 1.5 | kg.cm/cm | |
| 热性能 | 燃烧性 | 1/8 | IEC707 | FH3-25 | mm/min |
| 维卡软化点 | 1000g | ASTM D-1525 | 107 | ℃ | |
| 热变形温度 | 未退火 18.5kg/cm21/2〃 | ASTM D-648 | 98 | ℃ | |
| 燃烧性 | 1/8" | UL-94 | HB | ||
| 燃烧性 | 1/16〃 | UL-94 | HB | ||