PP日本住友AV-501 低温下高抗冲
| 洛氏硬度 | ASTM D785 | 95 | |||
| IZOD 缺口冲击强度 | 1/4" 23℃ | ASTM D256/ISO 179 | 45 | kg·cm/cm(J/M)ft·lb/in | |
| 1/4" -30℃ | ASTM D256/ISO 179 | 13 | kg·cm/cm(J/M)ft·lb/in | ||
| 1/8" 23℃ | ASTM D256/ISO 179 | 45 | kg·cm/cm(J/M)ft·lb/in | ||
| 1/8" -30℃ | ASTM D256/ISO 179 | 13 | kg·cm/cm(J/M)ft·lb/in | ||
| Charpy冲击强度 | 23℃ （缺口） | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | ||
| -30℃（缺口） | ASTM D256/ISO 179 | 13 | kg·cm/cm(J/M)ft·lb/in | ||
| 23℃（无缺口） | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | |||
| -30℃（无缺口） | ASTM D256/ISO 179 | 13 | kg·cm/cm(J/M)ft·lb/in | ||
| 物性性能 | 比重（密度） | ASTM D792/ISO 1183 | 0.90 | ||
| 成型收缩率 | ASTM D955 | 0.5-1.7 | % | ||
| 熔融指数（流动系数） | 200℃/5kg | ASTM D1238/ISO 1133 | 5.0 | g/10min | |
| 220℃/10kg | ASTM D1238/ISO 1133 | g/10min | |||
| 吸水率 23℃/24H | ASTM D570/ISO 62 | % | |||
| 热性能 | 热变形温度 | 退火 | ASTM D648/ISO 75 | 110 | ℃（℉） |
| 未退火 | ASTM D648/ISO 75 | ℃（℉） | |||
| 维卡软化点 | ASTM D1525/ISO R306 | ℃（℉） | |||
| 熔点 | - | ℃（℉） |