Shield-Bright 309LMo was designed for welding type 316 clad steels on the first pass in cladding steels or for welding dissimilar metals such as molybdenum-containing austenitic stainless steels to carbon steels. It is used in paper mills and in power plants to give greater corrosion resistance. This wire performs best when used out-of-position shielded with either Argon/CO2 or 100% CO2.
分类: |
E309LMoT1-1, SFA/AWS A5.22, Weld metal, E309LMoT1-4, SFA/AWS A5.22, Weld metal, TS309LMo-FB1, JIS Z 3323, Weld metal, YF309MoLC, KS D 3612, Weld metal, T 23 12 2 L P C1 2, EN ISO 17633-A, Weld metal, T 23 12 2 L P M21 2, EN ISO 17633-A, Weld metal |
认证: |
VL 309MoL, DNV-GL, RW 309MoLG(C), KR |
Approvals are based on factory location. Please contact ESAB for more information.
Alloy Type: |
C Cr Ni Mo |
Welding Current: |
DC+ |
焊缝金属分析
夏比V型缺口冲击性能
C1 Shielding Gas As welded |
Impact Value |
Testing Temperature |
50 J |
-29 °C |
20 J |
-196 °C |
Typical Tensile Properties
M21 Shielding Gas As welded |
Elongation |
Tensile Strength |
Yield Strength |
30 % |
750 MPa |
570 MPa |
C1 Shielding Gas As welded |
Elongation |
Tensile Strength |
Yield Strength |
35 % |
715 MPa |
550 MPa |
熔敷数据
安培 |
熔敷率 |
电压 V |
直径 |
送丝速度 |
130-220 A |
1.9-4.6 kg/h |
24-29 V |
1.2 mm |
5.8-14.4 m/min |